? The magnesia based curable specimens with different Si3N4 contents were casted using sintered magnesite (w(MgO)=95%) as starting material, SiO2 micro-powder as binder, 0.3%, 4% and 5% β-Si3N4 powder replacing the equal addition of magnesia powder respectively. The slag resistance test was carried out at 1550℃ for 3h using Baosteel tundish slag and static crucible method. The result indicates that: introducing Si3N4 could obviously improve the slag resistance of MgO based castable, which increased with increasing Si3N4. Dense SiO2 sintered layer formed on the surface of magnesia based castable because of the oxidation of Si3N4 addition, which can prevent the further slag penetration. In the deep inner of castable, the partial-pressure of oxygen was very low, so Si3N4 can exist stably. Meanwhile in reducing atmosphere, Si3N4 was hard to be sintered, which resulted in the loose interior structure of MgO based castable.