高中温窑具砖原料电熔镁铝尖晶石

高中温窑具砖原料电熔镁铝尖晶石基本信息

 

电熔镁铝尖晶石 Fused magnesium aluminum spinel

电熔镁铝尖晶石是以氧化铝粉和高纯轻烧氧化镁粉为主要原料，在电弧炉内经2000℃以上高温熔炼而成。本公司生产的电熔铝镁尖晶石有多个品级，可根据用户的要求，生产用户需要的产品。

电熔镁铝尖晶石具有体密大、热震稳定性好、抗侵蚀能力与抗渣性强的优点。它广泛应用于钢铁冶炼、水泥回转窑及玻璃工业窑炉上，是制造连铸滑板、水口砖、钢包衬砖和平炉砖的理想材料，也是大型水泥窑、中型水泥窑过渡带衬砖、耐火浇注料及高中温窑具砖的基本原料。

Fused magnesium aluminum spinel is produced by mixing the industrial alumina with the high-purity caustic-burned magnesia, smelting with high temperature more than 2000 degree centigrade in the electric-arc furnaces. And it can be processed into various sizes of particles according to the clients’ demands. Its grain is well developed with the

 features of compact texture and uniform structure, and there fore is the high-grade raw material for producing refractory products with high in density and good thermal shock resistance ( spinel and magnesia, etc. ).

Fused magnesium aluminum spinel has the characteristics of high bulk density,  high thermal shock resistance, strong corrosion

 resistance and slag- resistance. It is widely used in iron and steel melting, cement rotary kiln and glass furnace, as the ideal material for

 manufacturing cast sliding plate, nozzle bricks, ladle bricks and open hearth furnace bricks, as well as the basic material for ecotone bricks of large cement kilns, 

medium cement kilns, refractory castable materials, and first-class and medium-class kiln furniture.

 

本公司生产的镁铝尖晶石具体指标如下表Fused Magnesium Aluminum Spinel’s detailed indexes table:

性能/牌号properties/designation		AM-90	AM-80	AM-70
化学成分  chemical composition %	AL2O3	88-92	82-87	71-76
	MgO	8-12	12-17	22-27
	CaO	≤0.4	0.4	0.6
	Fe2O3	≤0.35	0.35	0.35
	SiO2	≤0.25	0.4	0.4
真密度 real density （g/m³）		≥3.3
段砂颗粒尺寸grain size of section sand （mm）		0-1/1-3/3-5/5-8
细粉 powder （目mesh）		-180  -220  -240  -320
用途 usage		生产耐火材料及精细陶瓷的重要原料，广泛用在炼钢电炉顶、转炉及钢包，大型水泥回转窑过渡带和玻璃蓄热室等耐材制品中。 As the important raw material for manufacturing refractory products and fine ceramics, widely used in refractory material products  as for making the steel furnace roofs, converters and ladles, the ecotone bricks of large rotary cement kiln, and the glass  furnace regenerators, etc.