关键词：magnesia refractory;high carbon Si Mn-killed;interface;inclusion;

内容简介

In the current study, the reaction between the industrial MgO refractory and the high carbon SiMn-killed steel was investigated using laboratory experiments. The penetration of the molten steel into the MgO refractory was small and the composition of inclusions in the steel changed very little after the reaction of 90 minutes. The penetration of the molten steel into MgO refractory at the interface was hardly detected. A new interface layer containing Al2O3 and MgO with the ...